Raw Elastomer Silicone Curing Agent Platinum Catalyzed Addition Cure In Bulk

C-100AB,two component platinum addition type cross linking agent which is added in the raw silicones for the cross linking of food and medical grade silicone rubber items ,The vulcanized products can pass the FDA test, ,it features with non-toxic, odourless, high grade of transparency, well anti-yellowing and other properties.

PRODUCT SPECIFICATION:

Good for both compression molding and extrusion forming. This agent are mainly applied to Food Grade and Medical Grade products, such as baby nipples, cake mold, silicone cookwares, extrusion gaskets ,ice mold, table matt, medical silicone tube and so on.

PRODUCT DETAILS:

C-100AB,two component platinum addition type cross linking agent

Which is added in the raw silicones for the cross linking of food and medical grade silicone rubber items ,

The vulcanized products can pass the FDA test,

it features with non-toxic, odourless, high grade of transparency, well anti-yellowing and other properties.

ATTENTION:

The raw material is easy poisoning once contact with nitrogen, phosphorus, sulfur and heavy metal materials.

C-100A and C-100B can not be added at the same time. First add C-100B into raw silicone and mixing evenly, then add C-100A into raw silicone. The addition order is important.

The temperature of mixing machine which used for mixing silicone with platinum curing agent can not be higher than 45℃. Please add this agent after being cold.

The mixed raw materials should be used up within two days

.Please choose the suitable raw materials for hot air vulcanization,unmatched raw material will cause bubbles in the process.

PROCESSING:

Type one: Extrusion Or Injection Moulding

1. For High Tear Strength Silicone Materials (filled with gaseous phase white carbon black) Application weight ratio:

C-100B 2.0~2.5%

C-100A 0.5~0.6%

Curing condition: IR(6meters),constant temperature ±5℃. First curing: IR curing at 190~200℃ for 40~60 seconds.

Finished curing: After first curing, it should be cured again as below conditions.

2. For Normal Silicone Material

Application weight ratio:

C-100B 1.5~2.0%

C-100A 0.5~0.6%

Curing condition:IR(6meters),constant temperature ±5℃.

First curing: IR(Infrared Radiation) curing at 140℃ for 40~50 seconds. Finished curing:After first curing, it should be cured again as below conditions.

Type two: Compression Molding

Application weight ratio:

C-100B 1.0~1.5%

C-100A 0.5%

Curing temperature: 115~135℃(200~300seconds)

Curing time:Can be adjusted with the thickness and type of the silicone products