Zero Initial Tack Thermoplastic Hot Press Glue for Industrial Coating

Szczegóły produktu

Miejsce pochodzenia: Guangdong, Chiny

Nazwa handlowa: Kanglibang

Orzecznictwo: RoHs,Reach

Warunki płatności i wysyłki

Minimalne zamówienie: 1 KG

Cena: negocjowalne

Szczegóły pakowania: 1 kg/butelka

Czas dostawy: 7-12 dni

Zasady płatności: T/T

Najlepszą cenę

Skontaktuj się teraz

Specyfikacje

Opis

Specyfikacje

Podkreślić: 
                                                                              zero initial tack hot melt adhesive, thermoplastic hot press glue, industrial coating hot melt adhesive
                                                  

Opis

Zero Initial Tack Thermoplastic Hot Press Glue for Industrial Coating

Product Description

Products Description

Synthesized with high-quality special resins, KL-17 modified hot melt adhesive fits coating on PET, PVC and PEI surfaces. It remains non-adhesive initially under room temperature, delivers excellent interfacial bonding via high-temperature pressing, and boasts versatile application scenarios and strong bonding force.

Application

Specification

Name	KL-17 Hot Melt Adhesive
Appearance	Colorless clear liquid
Main Raw Material	Special resin
Viscosity	500 ± 200 cps
Solid Content	32 ± 3%
Coating thickness	5 μm / 10 μm / 20 μm
Hard drying time	2 min / 4 min / 7 min
Storage condition	0–15℃, avoid heat and direct sunlight

Operating Steps

1. Ensure the substrate surface is clean, dust-free, and oil-free.  
2. Apply/screen print/spray the adhesive onto the substrate. 

3.Bake at 90-110 degrees Celsius for 1-2 minutes to evaporate solvents or moisture. 

4. A: Roll up (with cooling rollers) ☞ Apply release film ☞ For sale/Laminate within 6 months 
B: Lamination: Hot pressing (100-170 degrees Celsius for 1 minute) ☞ Curing (175 degrees Celsius for 40 minutes / 50-60 degrees
Celsius for 24 hours) 

5. After standing for 24 hours, conduct relevant tests.Packing & Delivery