High Temp & Boil Resistant PU Solvent Glue for Leather Fabric Bonding

Szczegóły produktu

Miejsce pochodzenia: Guangdong, Chiny

Nazwa handlowa: Kanglibang

Orzecznictwo: RoHs,Reach

Warunki płatności i wysyłki

Minimalne zamówienie: 1 KG

Cena: negocjowalne

Szczegóły pakowania: 1 kg/butelka

Czas dostawy: 7-12 dni

Zasady płatności: T/T

Najlepszą cenę

Skontaktuj się teraz

Specyfikacje

Opis

Specyfikacje

Podkreślić: 
                                                                              high temp PU solvent glue, boil resistant leather adhesive, fabric bonding hot melt adhesive
                                                  

Opis

High Temp & Boil Resistant PU Solvent Glue for Leather Fabric Bonding

Product Description

Products Description

KL-17 is one kind of modified hot melt adhesive based on special resin compounding and synthesis. It can be evenly coated on PET, PVC and PEI, without initial adhesion at room temperature. Great bonding can be achieved by high temperature pressure, along with wide application coverage and powerful adhesion.

Application

Specification

Name	KL-17 Hot Melt Adhesive
Appearance	Colorless clear liquid
Main Raw Material	Special resin
Viscosity	500 ± 200 cps
Solid Content	32 ± 3%
Coating thickness	5 μm / 10 μm / 20 μm
Hard drying time	2 min / 4 min / 7 min
Storage condition	0–15℃, avoid heat and direct sunlight

Operating Steps

1. Ensure the substrate surface is clean, dust-free, and oil-free.  
2. Apply/screen print/spray the adhesive onto the substrate. 

3.Bake at 90-110 degrees Celsius for 1-2 minutes to evaporate solvents or moisture. 

4. A: Roll up (with cooling rollers) ☞ Apply release film ☞ For sale/Laminate within 6 months 
B: Lamination: Hot pressing (100-170 degrees Celsius for 1 minute) ☞ Curing (175 degrees Celsius for 40 minutes / 50-60 degrees
Celsius for 24 hours) 

5. After standing for 24 hours, conduct relevant tests.Packing & Delivery