Liquid Modified Hot Melt Adhesive for PET PI PVC Film Lamination

Szczegóły produktu

Miejsce pochodzenia: Guangdong, Chiny

Nazwa handlowa: Kanglibang

Orzecznictwo: RoHs,Reach

Warunki płatności i wysyłki

Minimalne zamówienie: 1 KG

Cena: negocjowalne

Szczegóły pakowania: 1 kg/butelka

Czas dostawy: 7-12 dni

Zasady płatności: T/T

Najlepszą cenę

Skontaktuj się teraz

Specyfikacje

Opis

Specyfikacje

Podkreślić: 
                                                                              PET film lamination adhesive, hot melt adhesive for PVC, liquid modified adhesive for PI
                                                  

Opis

Liquid Modified Hot Melt Adhesive for PET PI PVC Film Lamination

Product Description

Products Description

This modified hot melt adhesive KL-17 adopts special resin as raw material for synthesis. It is suitable for coating on PET, PVC and PEI, with no initial adhesion at room temperature. High temperature pressing enables great bonding effect, and it enjoys a broad application range and outstanding adhesive power.

Application

Specification

Name	KL-17 Hot Melt Adhesive
Appearance	Colorless clear liquid
Main Raw Material	Special resin
Viscosity	500 ± 200 cps
Solid Content	32 ± 3%
Coating thickness	5 μm / 10 μm / 20 μm
Hard drying time	2 min / 4 min / 7 min
Storage condition	0–15℃, avoid heat and direct sunlight

Operating Steps

1. Ensure the substrate surface is clean, dust-free, and oil-free.  
2. Apply/screen print/spray the adhesive onto the substrate. 

3.Bake at 90-110 degrees Celsius for 1-2 minutes to evaporate solvents or moisture. 

4. A: Roll up (with cooling rollers) ☞ Apply release film ☞ For sale/Laminate within 6 months 
B: Lamination: Hot pressing (100-170 degrees Celsius for 1 minute) ☞ Curing (175 degrees Celsius for 40 minutes / 50-60 degrees
Celsius for 24 hours) 

5. After standing for 24 hours, conduct relevant tests.Packing & Delivery