High Temperature Resistant Oil Glue

Rincian produk

Tempat asal: Guangdong, Tiongkok

Nama merek: Kanglibang

Sertifikasi: RoHs,Reach

Syarat Pembayaran & Pengiriman

Kuantitas min Order: 1KG

Harga: Bisa dinegosiasikan

Kemasan rincian: 1KG/Botol

Waktu pengiriman: 7-12 hari

Syarat-syarat pembayaran: T/T

Dapatkan Harga Terbaik

Hubungi Sekarang

Spesifikasi

Deskripsi

Spesifikasi

Menyoroti: 
                                                                              high temperature resistant oil glue, hot melt adhesive liquid, heat resistant adhesive glue
                                                  

Deskripsi

High Temperature Resistant Oil Glue

Product Description

Products Description

Serving as a modified hot melt adhesive refined from special synthetic resins, KL-17 can be applied via coating onto PET, PVC and PEI. It lacks initial tack under room temperature conditions, bonds substrates perfectly under heat and pressure, and combines the advantages of broad application scope and ultra-strong bonding capacity.

Application

Specification

Name	KL-17 Hot Melt Adhesive
Appearance	Colorless clear liquid
Main Raw Material	Special resin
Viscosity	500 ± 200 cps
Solid Content	32 ± 3%
Coating thickness	5 μm / 10 μm / 20 μm
Hard drying time	2 min / 4 min / 7 min
Storage condition	0–15℃, avoid heat and direct sunlight

Operating Steps

1. Ensure the substrate surface is clean, dust-free, and oil-free.  
2. Apply/screen print/spray the adhesive onto the substrate. 

3.Bake at 90-110 degrees Celsius for 1-2 minutes to evaporate solvents or moisture. 

4. A: Roll up (with cooling rollers) ☞ Apply release film ☞ For sale/Laminate within 6 months 
B: Lamination: Hot pressing (100-170 degrees Celsius for 1 minute) ☞ Curing (175 degrees Celsius for 40 minutes / 50-60 degrees
Celsius for 24 hours) 

5. After standing for 24 hours, conduct relevant tests.Packing & Delivery
To better ensure the safety of your goods, professional, environmentally friendly, convenient and efficient packaging services will be provided.