No Tack Dry Film Forming Modified Hot Press Adhesive

Rincian produk

Tempat asal: Guangdong, Tiongkok

Nama merek: Kanglibang

Sertifikasi: RoHs,Reach

Syarat Pembayaran & Pengiriman

Kuantitas min Order: 1KG

Harga: Bisa dinegosiasikan

Kemasan rincian: 1KG/Botol

Waktu pengiriman: 7-12 hari

Syarat-syarat pembayaran: T/T

Dapatkan Harga Terbaik

Hubungi Sekarang

Spesifikasi

Deskripsi

Spesifikasi

Menyoroti: 
                                                                              dry film forming adhesive, modified hot press adhesive, hot melt adhesive liquid
                                                  

Deskripsi

No Tack Dry Film Forming Modified Hot Press Adhesive

Product Description

Products Description

KL-17 is a modified hot melt adhesive synthesised from a special resin, can be coated on PET, PVC or PEI, no initial adhesion at
room temperature, high temperature pressure can be very good mutual adhesion of the hot melt adhesive, a wide range of
applications, strong adhesion and other advantages.

Application

Specification

Name	KL-17 Hot Melt Adhesive
Appearance	Colorless clear liquid
Main Raw Material	Special resin
Viscosity	500 ± 200 cps
Solid Content	32 ± 3%
Coating thickness	5 μm / 10 μm / 20 μm
Hard drying time	2 min / 4 min / 7 min
Storage condition	0–15℃, avoid heat and direct sunlight

Operating Steps

1. Ensure the substrate surface is clean, dust-free, and oil-free.  
2. Apply/screen print/spray the adhesive onto the substrate. 

3.Bake at 90-110 degrees Celsius for 1-2 minutes to evaporate solvents or moisture. 

4. A: Roll up (with cooling rollers) ☞ Apply release film ☞ For sale/Laminate within 6 months 
B: Lamination: Hot pressing (100-170 degrees Celsius for 1 minute) ☞ Curing (175 degrees Celsius for 40 minutes / 50-60 degrees
Celsius for 24 hours) 

5. After standing for 24 hours, conduct relevant tests.Packing & Delivery
To better ensure the safety of your goods, professional, environmentally friendly, convenient and efficient packaging services will be provided.